Excellent Quality Steel Pipe Piles Of Cylindrical Shape - Cold Formed Pipes, EN10219 S235JRH, S235J0H, S355JRH, S355J0H – Spiral

steel grade

minimum yield strength
Mpa

Tensile strength

Minimum elongation
%

Minimum impact energy
J

Specified thickness
mm

Specified thickness
mm

Specified thickness
mm

at test temperature of

＜16

＞16≤40

＜3

≥3≤40

-20℃

0℃

20℃

235

225

360-510

360-510

24

-

-

27

275

265

430-580

410-560

20

-

27

-

27

-

-

365

345

510-680

470-630

20

-

27

-

27

-

-

40

-

-

Steel grade

Type of de-oxidation a

% by mass, maximum

Steel name

Steel number

C

C

Si

Mn

P

S

Nb

S235JRH

1.0039

FF

0,17

—

1,40

0,040

0,040

0.009

S275J0H

1.0149

FF

0,20

—

1,50

0,035

0,035

0,009

S275J2H

1.0138

FF

0,20

—

1,50

0,030

0,030

—

S355J0H

1.0547

FF

0,22

0,55

1,60

0,035

0,035

0,009

S355J2H

1.0576

FF

0,22

0,55

1,60

0,030

0,030

—

S355K2H

1.0512

FF

0,22

0,55

1,60

0,030

0,030

—

a. The deoxidation method is designated as follows:

FF: Fully killed steel containing nitrogen binding elements in amounts sufficient to bind available nitrogen (e.g. min. 0,020 % total Al or 0,015 % soluble Al).

b. The maximum value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,020 % with a minimum Al/N ratio of 2:1, or if sufficient other N-binding elements are present. The N-binding elements shall be recorded in the Inspection Document.