China Wholesale Double Welded Pipe - ASTM A234 WPB & WPC pipe fittings including elbows, tee, reducers – Spiral
Chemical Composition of ASTM A234 WPB & WPC Element Content, % ASTM A234 WPB ASTM A234 WPC Carbon [C] ≤0.30 ≤0.35 Manganese [Mn] 0.29-1.06 0.29-1.06 Phosphorus [P] ≤0.050 ≤0.050 Sulfur [S] ≤0.058 ≤0.058 Silicon [Si] ≥0.10 ≥0.10 Chromium [Cr] ≤0.40 ≤0.40 Molybdenum [Mo] ≤0.15 ≤0.15 Nickel [Ni] ≤0.40 ≤0.40 Copper [Cu] ≤0.40 ≤0.40 Vanadium [V] ≤0.08 ≤0.08 *The Carbon Equivalent [C.E.=C+Mn/6+(Cr+Mo... -
Super Lowest Price Stainless Pipe Welding - Fusion-Bonded Epoxy Coatings Awwa C213 Standard – Spiral
Physical properties of epoxy powder materials Specific gravity at 23℃: minimum 1.2 and maximum 1.8 Sieve analysis: maximum 2.0 Gel time at 200 ℃: less than 120s Abrasive blast cleaning Bare steel surfaces shall be abrasive blast-cleaned in accordance with SSPC-SP10/NACE No. 2 unless otherwise specified by the purchaser. The blast anchor pattern or profile depth shall be 1.5 mil to 4.0 mil(38 µm to 102 µm) measured in accordance with ASTM D4417. Preheating Pipe that has been cleaned shall be p... -
Hot Selling For Spiral Welded Pipe – Spirally welded steel pipes ASTM A252 grade 1 2 3 – Spiral
Mechanical Property Grade 1 Grade 2 Grade 3 Yield Point or yield strength, min, Mpa(PSI) 205(30 000) 240(35 000) 310(45 000) Tensile strength, min, Mpa(PSI) 345(50 000) 415(60 000) 455(66 0000) Product analysis The steel shall contain no more than 0.050% phosphorous. Permissible Variations In Weights and Dimensions Each length of pipe pile shall be weighed separately and its weight shall not vary more than 15% over or 5% under its theoretical weight, calculated using its length and... -
2021 China New Design Underground Pipe Line - Fusion-Bonded Epoxy Coatings Awwa C213 Standard – Spiral
Physical properties of epoxy powder materials Specific gravity at 23℃: minimum 1.2 and maximum 1.8 Sieve analysis: maximum 2.0 Gel time at 200 ℃: less than 120s Abrasive blast cleaning Bare steel surfaces shall be abrasive blast-cleaned in accordance with SSPC-SP10/NACE No. 2 unless otherwise specified by the purchaser. The blast anchor pattern or profile depth shall be 1.5 mil to 4.0 mil(38 µm to 102 µm) measured in accordance with ASTM D4417. Preheating Pipe that has been cleaned shall be p... -
New Arrival China Ss 304 Erw Pipe - ASTM A234 WPB & WPC pipe fittings including elbows, tee, reducers – Spiral
Chemical Composition of ASTM A234 WPB & WPC Element Content, % ASTM A234 WPB ASTM A234 WPC Carbon [C] ≤0.30 ≤0.35 Manganese [Mn] 0.29-1.06 0.29-1.06 Phosphorus [P] ≤0.050 ≤0.050 Sulfur [S] ≤0.058 ≤0.058 Silicon [Si] ≥0.10 ≥0.10 Chromium [Cr] ≤0.40 ≤0.40 Molybdenum [Mo] ≤0.15 ≤0.15 Nickel [Ni] ≤0.40 ≤0.40 Copper [Cu] ≤0.40 ≤0.40 Vanadium [V] ≤0.08 ≤0.08 *The Carbon Equivalent [C.E.=C+Mn/6+(Cr+Mo... -
Fast Delivery Domestic Water Piping - Fusion-Bonded Epoxy Coatings Awwa C213 Standard – Spiral
Physical properties of epoxy powder materials Specific gravity at 23℃: minimum 1.2 and maximum 1.8 Sieve analysis: maximum 2.0 Gel time at 200 ℃: less than 120s Abrasive blast cleaning Bare steel surfaces shall be abrasive blast-cleaned in accordance with SSPC-SP10/NACE No. 2 unless otherwise specified by the purchaser. The blast anchor pattern or profile depth shall be 1.5 mil to 4.0 mil(38 µm to 102 µm) measured in accordance with ASTM D4417. Preheating Pipe that has been cleaned shall be p... -
Manufacturer Of Underground Gas Line - Cold Formed Pipes, EN10219 S235JRH, S235J0H, S355JRH, S355J0H – Spiral
Mechanical Property steel grade minimum yield strength Mpa Tensile strength Minimum elongation % Minimum impact energy J Specified thickness mm Specified thickness mm Specified thickness mm at test temperature of ＜16 ＞16≤40 ＜3 ≥3≤40 ≤40 -20℃ 0℃ 20℃ S235JRH 235 225 360-510 360-510 24 - - 27 S275J0H 275 265 430-580 410-560 20 - 27 - S275J2H 27 - - S355J0H 365 345 510-680 470-630 20 - 27 - ... -
Factory Wholesale Welding Steel Pipe Together - ASTM A234 WPB & WPC pipe fittings including elbows, tee, reducers – Spiral
Chemical Composition of ASTM A234 WPB & WPC Element Content, % ASTM A234 WPB ASTM A234 WPC Carbon [C] ≤0.30 ≤0.35 Manganese [Mn] 0.29-1.06 0.29-1.06 Phosphorus [P] ≤0.050 ≤0.050 Sulfur [S] ≤0.058 ≤0.058 Silicon [Si] ≥0.10 ≥0.10 Chromium [Cr] ≤0.40 ≤0.40 Molybdenum [Mo] ≤0.15 ≤0.15 Nickel [Ni] ≤0.40 ≤0.40 Copper [Cu] ≤0.40 ≤0.40 Vanadium [V] ≤0.08 ≤0.08 *The Carbon Equivalent [C.E.=C+Mn/6+(Cr+Mo... -
Hot New Products Steel Pipe Pile Specifications - ASTM A234 WPB & WPC pipe fittings including elbows, tee, reducers – Spiral
Chemical Composition of ASTM A234 WPB & WPC Element Content, % ASTM A234 WPB ASTM A234 WPC Carbon [C] ≤0.30 ≤0.35 Manganese [Mn] 0.29-1.06 0.29-1.06 Phosphorus [P] ≤0.050 ≤0.050 Sulfur [S] ≤0.058 ≤0.058 Silicon [Si] ≥0.10 ≥0.10 Chromium [Cr] ≤0.40 ≤0.40 Molybdenum [Mo] ≤0.15 ≤0.15 Nickel [Ni] ≤0.40 ≤0.40 Copper [Cu] ≤0.40 ≤0.40 Vanadium [V] ≤0.08 ≤0.08 *The Carbon Equivalent [C.E.=C+Mn/6+(Cr+Mo... -
Factory Cheap Hot Welding Thin Wall Tubing - ASTM A234 WPB & WPC pipe fittings including elbows, tee, reducers – Spiral
Chemical Composition of ASTM A234 WPB & WPC Element Content, % ASTM A234 WPB ASTM A234 WPC Carbon [C] ≤0.30 ≤0.35 Manganese [Mn] 0.29-1.06 0.29-1.06 Phosphorus [P] ≤0.050 ≤0.050 Sulfur [S] ≤0.058 ≤0.058 Silicon [Si] ≥0.10 ≥0.10 Chromium [Cr] ≤0.40 ≤0.40 Molybdenum [Mo] ≤0.15 ≤0.15 Nickel [Ni] ≤0.40 ≤0.40 Copper [Cu] ≤0.40 ≤0.40 Vanadium [V] ≤0.08 ≤0.08 *The Carbon Equivalent [C.E.=C+Mn/6+(Cr+Mo... -
High Reputation Welding Aluminum Intercooler Piping - ASTM A234 WPB & WPC pipe fittings including elbows, tee, reducers – Spiral
Chemical Composition of ASTM A234 WPB & WPC Element Content, % ASTM A234 WPB ASTM A234 WPC Carbon [C] ≤0.30 ≤0.35 Manganese [Mn] 0.29-1.06 0.29-1.06 Phosphorus [P] ≤0.050 ≤0.050 Sulfur [S] ≤0.058 ≤0.058 Silicon [Si] ≥0.10 ≥0.10 Chromium [Cr] ≤0.40 ≤0.40 Molybdenum [Mo] ≤0.15 ≤0.15 Nickel [Ni] ≤0.40 ≤0.40 Copper [Cu] ≤0.40 ≤0.40 Vanadium [V] ≤0.08 ≤0.08 *The Carbon Equivalent [C.E.=C+Mn/6+(Cr+Mo... -
2021 China New Design Sanitary Pipe Welding - Seamless Carbon Steel Pipes ASTM A106 Gr.B – Spiral
Mechanical property of the A106 seamless pipes Chemical position of the A106 pipes Heat treatment Hot-finished pipe need not be heat treated. When hot-finished pipes is heat treated, it shall be treated at a temperature of 650℃ or higher. Bending test required. Flattening test is not required. Hydrostatic test is not mandatory. As an alternative to the hydrostatic test at the option of the manufacturer or where specified in the PO, it shall be permissible for the full body of each pipe to b...